Products
Inorganic Two-component High and Low Temperature Resistant Binder
Inorganic two-component high and low temperature resistant binder made of inorganic reinforcing powder, minerals, curing agent, additives and other raw materials.
It is used for bonding foam glass, polyurethane, polyisocyanurate and other insulation materials, with a wide range of using temperature. Powder-A and liquid-B should be mixed.
| Color | Densities | Bonding strength | low temperature testing | High temperature testing |
Powder-A gray-black powder Liquid-B semi-transparent gel | 800~ 900kg/m3 | >0.1MPa（20℃） | -196℃ ,3 hours, no cracking, no shedding | +800℃, 3 hours, no flow, no shedding |
A material: woven bag, 25kg/bag.
B material: packed in iron drum, 18kg/drum.
Keep it in room temperature and keep it away from light.
Before use, mix the AB components evenly, mixing ratio (mass ratio): Powder-A: Liquid-B=13:7 with a spatula and apply evenly on the substrate.
The product should be mixed well with A/B components before use, and used up within 2 hours after mixing, so please estimate the dosage before mixing to avoid unnecessary waste.
Please use up the product within 24 hours after opening, if you can not use up the product, please keep the remaining product sealed.